DE2612664A1 - BUILDING MATERIAL - Google Patents
BUILDING MATERIALInfo
- Publication number
- DE2612664A1 DE2612664A1 DE19762612664 DE2612664A DE2612664A1 DE 2612664 A1 DE2612664 A1 DE 2612664A1 DE 19762612664 DE19762612664 DE 19762612664 DE 2612664 A DE2612664 A DE 2612664A DE 2612664 A1 DE2612664 A1 DE 2612664A1
- Authority
- DE
- Germany
- Prior art keywords
- building material
- material according
- fatty alcohol
- alcohol
- free
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Description
Hoechst AktiengesellschaftHoechst Aktiengesellschaft
- 3-HOE 76/H 011- 3-HOE 76 / H 011
BaustoffmasseBuilding material mass
Die vorliegende Erfindung betrifft eine Baustoffmasse auf der Grundlage von Calciumsulfat und Wasser und ein Verfahren zur Herstellung eines fließfähigen Materials sowie die Verwendung dieses Materials für selbstnivellierende Estriche.The present invention relates to a building material based on calcium sulfate and water and a method for the production of a flowable material as well as the use of this material for self-leveling Screeds.
Das Verlegen eines Nutzbodens, beispielsweise aus Fliesen oder Holzparkett, ist nur auf einer horizontalen und ebenen Oberfläche, nicht jedoch auf den meist unebenen und rauhen Rohdecken von Gebäuden möglich.Laying a useful floor, for example made of tiles or wooden parquet, is only possible on a horizontal and level Surface, but not possible on the mostly uneven and rough ceilings of buildings.
Während früher zur Herstellung der erforderlichen horizontalen und ebenen Oberfläche Estriche aus Gußasphalt, Zement oder Magnesit verwendet wurden, deren Aufbringen, Nivellie-, ren und Glätten einen beträchtlichen Arbeitsaufwand mit sich bringen, sind seit einiger Zeit Mörtelmischungen bekannt, welche nach Zugabe von Wasser eine fließ- und pumpfähige Kosistenz aufweisen und sich unter dem Einfluß der Schwerkraft wie eine Flüssigkeit selbst nivellieren und glätten.While earlier to create the necessary horizontal and even surface screeds from mastic asphalt, cement or magnesite were used, their application, leveling, leveling and smoothing a considerable amount of work mortar mixtures have been known for some time which, after adding water, become flowable and pumpable Have consistency and level and self-leveling under the influence of gravity like a liquid smooth.
So ist aus der DT-OS 1 943 634 eine Mörtelmasse bekannt, welche aus Anhydrit und gegebenenfalls Sand sowie einerFor example, a mortar mass is known from DT-OS 1 943 634, which of anhydrite and optionally sand as well as a
- 2 709839/0448 - 2 709839/0448
— 2. —- 2. -
- t. - t.
die Sedimentation der Feststoffe in Wasser verzögernden und einer die Festigkeit der aushärtenden Masse erhöhenden Substanz besteht, wobei als die die Festigkeit erhöhende Substanz ein sulfit- oder sulfonsäuremodifiziertes Harz auf der Basis eines Amino-s-triazins mit mindestens zwei Aminogruppen geeignet ist. Nach Versetzen dieser Mischung mit Wasser wird eine fließfähige Masse erhalten, welche nach Ausgießen auf eine tragende Unterlage unter Bildung einer horizontalen Oberfläche auseinanderfließt und in diesem Zustand erstarrt.the sedimentation of the solids in water retards and one that increases the strength of the hardening mass Substance consists, with a sulfite- or sulfonic acid-modified resin as the strength-increasing substance based on an amino-s-triazine with at least two amino groups is suitable. After adding this mixture with water, a flowable mass is obtained which, after pouring onto a supporting base, forms flows apart on a horizontal surface and into frozen in this state.
Weiterhin wird in der DT-OS 2 359 290 eine Baustoffmasse vorgeschlagen, welche aus Calciumsulfat-ß-Halbhydrat, Tonerdeschmelzzement und/oder Portlandzement, dem o.g. modifizierten Harz auf der Basis von Amino-s-triazin als festigkeitserhöhende Substanz sowie einem Abbindeverzögerer und/oder einem Füllstoff besteht, wobei als festigkeitserhöhende Substanz pulverförmige mit Sulfit oder Sulfonsäure modifizierte Melamin-Formaldehyd-Kondensationsprodukte, beispielsweise Melment^-'F10, besonders geeignet sind. Diese Baustoffmasse wird mit Wasser in der für die Fließfähigkeit erforderlichen Menge versetzt.Furthermore, in DT-OS 2 359 290 a building material is proposed, which consists of calcium sulfate-ß-hemihydrate, Alumina cement and / or Portland cement, the above-mentioned modified resin based on amino-s-triazine as strength-increasing substance as well as a setting retarder and / or a filler, wherein as strength-increasing Substance powdered melamine-formaldehyde condensation products modified with sulphite or sulphonic acid, for example Melment ^ - 'F10, are particularly suitable. This building material mass is mixed with water in the for the required amount is added to the flowability.
Schließlich ist aus der DT-OS 2 322 707 eine Mörtelmischung bekannt, welche aus Anhydrit und Sand sowie Kaliumsulfat und Eisensulfat als Anreger besteht und welche als Fließmittel Kondensationsprodukte aus Formaldehyd mit sulfonierten aromatischen Äthern, Iminen oder SuIfonen enthält.Finally, from DT-OS 2 322 707 a mortar mixture is known which consists of anhydrite and sand and potassium sulfate and iron sulfate as a stimulator and which as a flow agent is condensation products of formaldehyde with sulfonated aromatic ethers, imines or sulfones.
Nachteilig ist bei den bisher bekannten Baustoffmassen auf der Grundlage von Calciumsulfat, daß sie neben die Festigkeit erhöhenden, teilweise kompliziert aufgebauten organischen Substanzen zusätzliche Stoffe als Verflüssiger enthalten müssen, um selbstnivellierend zu sein.The disadvantage of the previously known building materials based on calcium sulfate is that they are not only strength but also strength increasing, sometimes complex organic substances contain additional substances as liquefiers need to be self-leveling.
9839/0448 - 3 -9839/0448 - 3 -
Es ist daher Aufgabe der vorliegenden Erfindung, eine Baustoffmasse auf der Grundlage von Calciumsulfat und Wasser anzugeben, bei welcher die selbstnivellierende Eigenschaft allein durch eine synergistisch wirkende Substanz erreicht wird, wobei auf den Zusatz von Magerungsmitteln im Interesse einer guten Fließfähigkeit und auf Zugabe teurer Substanzen zur Erhöhung der Endfestigkeit verzichtet werden soll. Das wird erfindungsgemäß dadurch erreicht, daß die Baustoffmasse einen oder mehrere Fettalkohol-Polyglykoläther und/oder Synthesealkohol-Polyglykoläther enthält, wobei der Gehalt dieser Stoffe, bezogen auf die CaI-ciumsulfat-Wasser-Mischung, 0,1 bis 5 Gewichts^, vorzugsweise 0,5 bis 3 Gewichts%, beträgt.It is therefore the object of the present invention to provide a building material composition on the basis of calcium sulphate and water to indicate at which the self-leveling property is achieved solely by a synergistic substance, with the addition of weight loss agents im In the interest of good flowability and the addition of expensive substances to increase the final strength are dispensed with target. This is achieved according to the invention in that the building material is one or more fatty alcohol polyglycol ethers and / or synthetic alcohol polyglycol ether, the content of these substances, based on the calcium sulfate-water mixture, 0.1 to 5% by weight, preferably 0.5 to 3% by weight.
Die Baustoffmasse gemäß der Erfindung kann wahlweise auch noch dadurch gekennzeichnet sein, daßThe building material composition according to the invention can optionally also be characterized in that
a) als Fettalkohol-Polyglykoläther Umsetzungsprodukte von 1 bis 20 Mol Äthylenoxid je Mol Fettalkohol dienen,a) the fatty alcohol polyglycol ethers are reaction products of 1 to 20 moles of ethylene oxide per mole of fatty alcohol,
b) der Fettalkohol Cocosfettalkohol ist,b) the fatty alcohol is coconut fatty alcohol,
c) der Fettalkohol Oleylalkohol ist,c) the fatty alcohol is oleyl alcohol,
d) der Fettalkohol Stearylalkohol ist,d) the fatty alcohol is stearyl alcohol,
e) als Synthesealkohol-Polyglykoläther Umsetzungsprodukte von 1 bis 2 Mol Äthylenoxid je Mol Synthesealkohol dienen,e) as synthetic alcohol-polyglycol ethers, reaction products serve from 1 to 2 moles of ethylene oxide per mole of synthetic alcohol,
f) der Synthesealkohol Isotridekanol ist,f) the synthetic alcohol is isotridekanol,
- 4 709839/0448 - 4 709839/0448
— ^. —- ^. -
g) sie 0,2 bis 1 Gewichts%, vorzugsweise 0,3 bis 0,7 Gewichts^, bezogen auf die Calciumsulfat-Wasser-Mischung, eines Antischaummittels enthält.g) they 0.2 to 1% by weight, preferably 0.3 to 0.7% by weight, based on the calcium sulfate-water mixture, contains an anti-foam agent.
Eine freifließende Masse ist aus der erfindungsgemäßen Baustoffmasse dadurch herstellbar, daß man sie chargenweise in eine Mischzone einbringt und darin unter Rühren mit einer Umfangsgeschwindigkeit von 80 bis 750 m/min 2 bis 15 Minuten vermischt; daß man die gemischte Masse in eine mit einer Umfangsgeschwindigkeit von 25 bis 90 m/min bewegte Vorratszone überführt; und daß man die Masse aus der Vorratszone kontinuierlich entnimmt und zum Verlegeort pumpt.A free-flowing mass is made from the building material mass according to the invention can be produced by introducing them in batches into a mixing zone and taking them there with stirring mixed at a peripheral speed of 80 to 750 m / min for 2 to 15 minutes; that you can convert the mixed mass into a transferred at a circumferential speed of 25 to 90 m / min moving storage zone; and that you can get the crowd out of the The storage zone is continuously withdrawn and pumped to the installation site.
Schließlich ist die freifließende Masse für selbstnivellierende Estriche zur Bildung von Bodenbelägen mit porenfreier und glatter Oberfläche verwendbar.Finally, the free flowing mass is for self-leveling Screeds can be used to form floor coverings with a pore-free and smooth surface.
Als Calciumsulfat kann, die erfindungsgemäße Baustoffmasse sowohl die wasserfreie Form (Anhydrit) als auch das Halbhydrat (in der α- oder ß-Form) enthalten. Dabei ist jedoch nur ein solcher Anhydrit verwendbar, welcher der Güteklasse AB 200 nach DIN 4208 (Ausgabe Oktober 1962) entspricht, während das Calciumsulfat-Halbhydrat einen Wassergipswert (bestimmt nach DIN 1168, Teil 2, Seite 3; Ausgabe Juli 1975) von 0,37 bis 0,50 aufweisen muß.The building material composition according to the invention can be used as calcium sulfate contain both the anhydrous form (anhydrite) and the hemihydrate (in the α- or ß-form). However, there is only an anhydrite can be used which corresponds to quality class AB 200 according to DIN 4208 (October 1962 edition), while the calcium sulfate hemihydrate has a water gypsum value (determined in accordance with DIN 1168, part 2, page 3; July 1975 edition) must have from 0.37 to 0.50.
Als Anreger kann die Baustoffmasse gemäß der Erfindung Alkalisulfate, insbesondere des Kaliums, enthalten.The building material composition according to the invention can contain alkali sulfates, in particular of potassium, as stimulators.
Für die Beurteilung der Selbstnivellierung der aus der erfindungsgemäßen Baustoffmasse hergestellten freifließenden Masse ist das Ausbreitmaß geeignet, welches nach der Ausbreitmethode bestimmt wird.For the assessment of the self-leveling from the inventive Building material produced free-flowing mass, the slump is suitable, which according to the spreading method is determined.
709839/0448 - 5 -709839/0448 - 5 -
Λ·Λ ·
Hierzu wird eine Scheibe aus Glas oder Plexiglas von etwa 30 cm Durchmesser mit einem Maßkreuz versehen, dessen Nullpunkt in der Mitte der Scheibe liegt. Auf das Maßkreuz wird ein Hartgummiring nach DIN 1164 (vergl. Blatt 5, Ausgabe Juni 1970) aufgesetzt und mit der fließfähigen Mischung randvoll gefüllt. Nach Abheben des Ringes breitet sich die Mischung nach allen Seiten aus. Mit Hilfe des Maßkreuzes wird der Durchmesser der ausgebreiteten Mischung dann ermittelt, wenn die Mischung zu fließen aufgehört hat. Dieser in cm angegebene Durchmesser ist das Ausbreitmaß.For this purpose, a disk made of glass or plexiglass with a diameter of about 30 cm is provided with a measuring cross Zero point is in the middle of the disc. A hard rubber ring according to DIN 1164 (see page 5, edition June 1970) and filled to the brim with the flowable mixture. After lifting the ring spreads the mixture works out in all directions. With the help of the measuring cross, the diameter of the spread mixture is determined then determined when the mixture has stopped flowing. This diameter, given in cm, is the slump.
Die freifließende Masse für einen selbstnivellierenden Estrich muß ein Ausbreitmaß von mindestens 25 cm aufweisen, um gut verarbeitbar zu sein.The free-flowing mass for a self-leveling screed must have a slump of at least 25 cm, to be easy to process.
Die Erfindung sei nunmehr anhand von Beispielen erläutert.The invention will now be explained on the basis of examples.
3 500 g Anhydrit, 45 g KpSO, als Anreger, 60 g Genapol^ X-O5O (Isotridekanol-Polyglykoläther mit 5 Mol Äthylenoxid je Mol Isotridekanol; HOECHST) und 912 g Wasser wurden innig vermischt.3 500 g anhydrite, 45 g KpSO, as a stimulator, 60 g Genapol ^ X-O5O (Isotridekanol polyglycol ether with 5 moles of ethylene oxide per mole of isotridekanol; HOECHST) and 912 g of water were mixed intimately.
Die resultierende freifließende Masse hatte ein Ausbreitmaß von 30 cm.The resulting free-flowing mass had a slump of 30 cm.
An aus der freifließenden·Masse angefertigten Probekörpern mit Abmessungen von 40 χ 40 χ 160 mm (nach DIN 1168, Teil 2, Seiten 4 und 5; Ausgabe Juli 1975) wurde nach Trocknung bis zur Gewichtskonstanz bei einer Dichte von 1,2 bis 1,3 g/cm eine BiegeZugfestigkeit von 25 bis 30 kp/cm ermittelt. On test specimens made from the free-flowing mass with dimensions of 40 χ 40 χ 160 mm (according to DIN 1168, part 2, pages 4 and 5; edition July 1975) after drying A flexural tensile strength of 25 to 30 kp / cm is determined up to constant weight at a density of 1.2 to 1.3 g / cm.
709839/0448709839/0448
3500 g Anhydrit, 45 g KpSO, als Anreger, 15 g SP3 (im wesentlichen Dimethylpolysiloxan; WACKER) als Antischaummittel, 60 g Genapolw X-050 und 912 g Wasser wurden innig vermischt.3500 g anhydrite, 45 g KpSO, as a stimulator, 15 g SP3 (essentially Dimethylpolysiloxane; WACKER) as an antifoam agent, 60 g Genapolw X-050 and 912 g water were mixed intimately.
Die resultierende freifließende Masse hatte ein Ausbreitmaß von 27 bis 28 cm.The resulting free-flowing mass had a slump of 27 to 28 cm.
An aus der freifließenden Masse angefertigten Probekörpern mit Abmessungen von 40 χ 40 χ 16O mm (nach DIN 1168, Teil 2; Ausgabe Juli 1975) wurde nach Trocknung bis zur Gewichtskonstanz bei einer Dichte von 1,8 bis 1,9 g/cmOn test specimens made from the free-flowing mass with dimensions of 40 40 χ 160 mm (according to DIN 1168, Part 2; July 1975 edition) was dried to constant weight at a density of 1.8 to 1.9 g / cm
eine Biegezugfestigkeit von ^ bis 65 kp/cm ermittelt.a flexural strength of ^ to 65 kp / cm was determined.
3500 g Anhydrit, 45 g K2SO4 als Anreger, 15 g SP3 (WACKER)3500 g anhydrite, 45 g K 2 SO 4 as a stimulator, 15 g SP3 (WACKER)
1 R1 als Antischaummittel, 60 g Genapolw C-050 (Cocosfettalkoholpolyglykoläther, vorwiegend C^2 bis ci4> m^ 5 Mol Äthylenoxid je Mol Cocosfettalkohol; HOECHST) und 912 g Wasser wurden innig vermischt.1 R1 as an antifoam agent, 60 g of Genapolw C-050 (coconut fatty alcohol polyglycol ether, predominantly C ^ 2 to c i4> m ^ 5 mol of ethylene oxide per mole of coconut fatty alcohol; HOECHST) and 912 g of water were intimately mixed.
Die resultierende freifließende Masse hatte ein Ausbreitmaß von 26 bis 27 cm.The resulting free-flowing mass had a slump of 26 to 27 cm.
An aus der freifließenden Masse angefertigten Probekörpern mit Abmessungen von 40 χ 40 χ 160 mm (nach DIN 1168, Teil 2; Ausgabe Juli 1975) wurde nach Trocknung bis zur Gewichtskonstanz bei einer Dichte von 1,8 bis 1,9 g/cm eine Biege- On test specimens made from the free-flowing mass with dimensions of 40 40 χ 160 mm (according to DIN 1168, part 2; July 1975 edition), after drying to constant weight at a density of 1.8 to 1.9 g / cm, a bending
Zugfestigkeit von 60 bis 65 kp/cm ermittelt.Tensile strength determined from 60 to 65 kp / cm.
3500 g Anhydrit, 45 g KpSO/, als Anreger, 15 g SP3 (WACKER)3500 g anhydrite, 45 g KpSO /, as a stimulator, 15 g SP3 (WACKER)
(kV(kV
als Antischaummittel, 60 g Genapol^0-050 (Oleylalkohol-as an anti-foam agent, 60 g Genapol ^ 0-050 (oleyl alcohol
- 7 -709839/0448- 7 -709839/0448
polyglykoläther, überwiegend ungesättigter C^g-Fettalkohol, mit 5 Mol Äthylenoxid je Mol Oleylalkohol; HOECHST) und 912 g Wasser wurden innig vermischt.polyglycol ether, predominantly unsaturated C ^ g fatty alcohol, with 5 moles of ethylene oxide per mole of oleyl alcohol; HOECHST) and 912 g of water were mixed intimately.
Die resultierende freifließende Masse hatte ein Ausbreitmaß von 27 bis 28 cm.The resulting free-flowing mass had a slump of 27 to 28 cm.
An aus der freifließenden Masse angefertigten Probekörpern mit Abmessungen von 40 χ 40 χ 160 mm (nach DIN 1168, Teil 2; Ausgabe Juli 1975) wurde nach Trocknung bis zur Gewichtskonstanz bei einer Dichte von 1,8 bis 1,9 g/cm eine Biegezugfestigkeit von 50 bis 60 kp/cm ermittelt.On test specimens made from the free-flowing mass with dimensions of 40 40 χ 160 mm (according to DIN 1168, part 2; July 1975 edition) became after drying to constant weight at a density of 1.8 to 1.9 g / cm Bending tensile strength determined from 50 to 60 kp / cm.
3500 g Anhydrit, 45 g KoSO^ als Anreger, 20 g Wacker-Silicon-Anti schaummittel SHvS), 60 g Genapol (5) S-050 (Stearylalkoholpolyglykoläther, gesättigte C^g- bis C1Q-Fettalkohole, mit 5 Mol Äthylenoxid je Mol Stearylalkohol; HOECHST) und 912 g Wasser wurden innig vermischt. Die resultierende freifließende Masse hatte ein Ausbreitmaß von 26 bis 27 cm.3500 g anhydrite, 45 g KoSO ^ as a stimulator, 20 g Wacker silicone anti-foam agent SHvS), 60 g Genapol (5) S-050 (stearyl alcohol polyglycol ether, saturated C ^ g to C 1Q fatty alcohols, with 5 moles of ethylene oxide each Moles of stearyl alcohol; HOECHST) and 912 g of water were intimately mixed. The resulting free-flowing mass had a slump of 26 to 27 cm.
An aus der freifließenden Masse angefertigten Probekörpern mit Abmessungen von 40 χ 40 χ 16O mm (nach DIN 1168, Teil 2; Ausgabe Juli 1975) wurde nach Trocknung bis zur Gewichtskonstanz bei einer Dichte von 1,7 bis 1,8 g/cm eine Biegezugfestigkeit von 55 bis 60 kp/cm ermittelt.On test specimens made from the free-flowing mass with dimensions of 40 40 χ 160 mm (according to DIN 1168, part 2; July 1975 edition) was dried to constant weight at a density of 1.7 to 1.8 g / cm a flexural strength of 55 to 60 kp / cm was determined.
3500 g Anhydrit, 45 g K2SO^ als Anreger, 15 g EH 4888
(20 #ige Emulsion eines modifizierten Siloxanes; GOLDSCHMIDT) als Antischaummittel, 60 g einer Mischung von Genapol^X-050
und Genapolv5)0-050 im Gewicht
Wasser wurden innig vermischt.3500 g anhydrite, 45 g K 2 SO ^ as a stimulator, 15 g EH 4888 (20 # emulsion of a modified siloxane; GOLDSCHMIDT) as an antifoam agent, 60 g of a mixture of Genapol ^ X-050 and Genapolv5) 0-050 in weight
Water were mixed intimately.
und Genapolv5)0-050 im Gewichtsverhältnis 1:1 sowie 912 gand Genapolv5) 0-050 in a weight ratio of 1: 1 and 912 g
- 8 709839/0448 - 8 709839/0448
• /ίοx • / ίο x
Die resultierende freifließende Masse hatte ein Ausbreitmaß von 28 cm.The resulting free-flowing mass had a slump of 28 cm.
An aus der freifließenden Masse angefertigten Probekörpern mit Abmessungen von 40 χ 40 χ 160 mm (nach DIN 1168, Teil 2; Ausgabe Juli 1975) wurde nach Trocknung bis zur Gewichtskonstanz bei einer Dichte von 1,7 bis 1,8 g/cm eineOn test specimens made from the free-flowing mass with dimensions of 40 40 χ 160 mm (according to DIN 1168, part 2; July 1975 edition) after drying to constant weight at a density of 1.7 to 1.8 g / cm a
BiegeZugfestigkeit von 55 bis 65 kp/cm ermittelt.Bending tensile strength determined from 55 to 65 kp / cm.
2000 g Calciumsulfat-a-Halbhydrat, 0,4 g Zitronensäure als Abbindeverzögerer, 60 g Genapol® X-050, 15 g EH 4888 (GOLDSCHMIDT) als Antischaummittel und 912 g Wasser wurdenK innig vermischt.2000 g calcium sulphate-a-hemihydrate, 0.4 g of citric acid as a retardant, 60 g of Genapol® X-050, 15 g of EH 4888 (GOLDSCHMIDT) as an antifoaming agent and 912 g of water were mixed intimately K.
Die resultierende freifließende Masse hatte ein Ausbreitmaß von 26 bis 27 cm.The resulting free-flowing mass had a slump of 26 to 27 cm.
An aus der freifließenden Masse angefertigten Probekörpern mit Abmessungen von 40 χ 40 χ 160 mm (nach DIN 1168, Teil 2; Ausgabe Juli 1975) wurde nach Trocknung bis zur Gewichtskonstanz bei einer Dichte von 1,8 bis 1,9 g/cm eineOn test specimens made from the free-flowing mass with dimensions of 40 χ 40 χ 160 mm (according to DIN 1168, part 2; edition July 1975) after drying to constant weight at a density of 1.8 to 1.9 g / cm
Biegezugfestigkeit von 55 bis 70 kp/cm ermittelt.Bending tensile strength determined from 55 to 70 kp / cm.
1200 g Calciumsulfat-ß-Halbhydrat, 60 g Genapol® X-050, 15 g EH 4888 (GOLDSCHMIDT) als Antischaummittel und 912 g Wasser wurden innig vermischt.1200 g calcium sulfate ß-hemihydrate, 60 g Genapol® X-050, 15 g of EH 4888 (GOLDSCHMIDT) as an antifoam and 912 g of water were intimately mixed.
Die resultierende freifließende Masse hätte ein Ausbreitmaß von 26 bis 27 cm.The resulting free-flowing mass would have a slump of 26 to 27 cm.
An aus der freifließenden Masse angefertigten Probekörpern mit Abmessungen von 40 χ 40 χ 160 mm (nach DIN 1168, Teil 2; Ausgabe Juli 1975) wurde nach Trocknung bis zur Gewichtskonstanz bei einer Dichte von 1,0 bis 1,1 g/cm eineOn test specimens made from the free-flowing mass with dimensions of 40 40 χ 160 mm (according to DIN 1168, part 2; July 1975 edition) after drying to constant weight at a density of 1.0 to 1.1 g / cm a
Biegezugfestigkeit von 32 bis 38 kp/cm ermittelt.Bending tensile strength determined from 32 to 38 kp / cm.
709839/0448709839/0448
Claims (10)